K. D. Ralston, J. G. Brunner, and S. Virtanen et al.
Recent works on high-purity materials have indicated that microstructural modification via grain refinement can alternately reduce or enhance corrosion, depending on the specific material-environment combination. Generally, however, a paucity of information exists in understanding how microstructu ... [Corrosion 67, 105001 (2011)] published Sat Oct 01, 2011.

[Read the rest of this article...]

Posted in: Corrosion
Actions: E-mail | Permalink |
20
S. Holmes, A. Roberts, and G. Glass et al.
This work examines the current response of installed “hybrid” (combined impressed current and sacrificial) anodes to changes in environmental conditions and investigates the effect of this “responsive behavior” on anode life span. The behavior reported is also discussed in terms of its correlation ... [Corrosion 67, 105005 (2011)] published Sat Oct 01, 2011.

[Read the rest of this article...]

Posted in: Corrosion
Actions: E-mail | Permalink |
20
E. Sarmiento, J. Uruchurtu, and J. G. González-Rodriguez et al.
The corrosion behavior of Type 316L (UNS S31603) stainless steel in a lithium bromide (LiBr) + ethylene glycol (C2H6O2) + H2O solution at different temperatures was evaluated using electrochemical noise and electrochemical impedance spectroscopy. The evaluation was performed from the fractal dimen ... [Corrosion 67, 105004 (2011)] published Sat Oct 01, 2011.

[Read the rest of this article...]

Posted in: Corrosion
Actions: E-mail | Permalink |
20
A. -R. Grayeli and H. Savaloni
AISI 304 (UNS S30400) and AISI 316 (UNS S31600) stainless steels were coated with a 250 run Ni film by electron beam deposition and post-annealed at different temperatures with a flow of 600 cm3 min−1 Ni. The samples were corrosion tested in 1.0 M sulfuric acid (H2SO4) solution using a potentiodyn ... [Corrosion 67, 105003 (2011)] published Sat Oct 01, 2011.

[Read the rest of this article...]

Posted in: Corrosion
Actions: E-mail | Permalink |
20
M. E. Nicho, M. G. Medrano-Baca, and U. León-Silva et al.
The effect of an adhesion promoter (2-[thiophen-3-yl]ethyl phosphonic acid [C6H9O3PS]) in the corrosion protection of 1018 (UNS G10180) mild steel by using poly(3-hexylthiophene) (P3HT) coatings in 0.5 M sulfuric acid (H2SO2) solution was studied. Mirror-abraded steels were pretreated with the adh ... [Corrosion 67, 105002 (2011)] published Sat Oct 01, 2011.

[Read the rest of this article...]