E. Sarmiento, J. Uruchurtu, and J. G. González-Rodriguez et al.
The corrosion behavior of Type 316L (UNS S31603) stainless steel in a lithium bromide (LiBr) + ethylene glycol (C2H6O2) + H2O solution at different temperatures was evaluated using electrochemical noise and electrochemical impedance spectroscopy. The evaluation was performed from the fractal dimen ... [Corrosion 67, 105004 (2011)] published Sat Oct 01, 2011.

[Read the rest of this article...]

Posted in: Corrosion
Actions: E-mail | Permalink |
20
A. -R. Grayeli and H. Savaloni
AISI 304 (UNS S30400) and AISI 316 (UNS S31600) stainless steels were coated with a 250 run Ni film by electron beam deposition and post-annealed at different temperatures with a flow of 600 cm3 min−1 Ni. The samples were corrosion tested in 1.0 M sulfuric acid (H2SO4) solution using a potentiodyn ... [Corrosion 67, 105003 (2011)] published Sat Oct 01, 2011.

[Read the rest of this article...]

Posted in: Corrosion
Actions: E-mail | Permalink |
20
M. E. Nicho, M. G. Medrano-Baca, and U. León-Silva et al.
The effect of an adhesion promoter (2-[thiophen-3-yl]ethyl phosphonic acid [C6H9O3PS]) in the corrosion protection of 1018 (UNS G10180) mild steel by using poly(3-hexylthiophene) (P3HT) coatings in 0.5 M sulfuric acid (H2SO2) solution was studied. Mirror-abraded steels were pretreated with the adh ... [Corrosion 67, 105002 (2011)] published Sat Oct 01, 2011.

[Read the rest of this article...]

Posted in: Corrosion
Actions: E-mail | Permalink |
22
A. M. Al-Turkustani, S. T. Arab, and A. A. Al-Rehaili
The effect of chloride ion addition on the corrosion and corrosion inhibition of mild steel in 1.0 M sulfuric acid (H2SO4) containing 10% ethanol (EtOH) at 30°C in the absence and presence of aqueous and/or alcoholic extracts of Zizyphus spina-christi (ZSC) plant have been investigated using chemi ... [Corrosion 67, 095004 (2011)] published Thu Sep 01, 2011.

[Read the rest of this article...]

Posted in: Corrosion
Actions: E-mail | Permalink |
22
P. Castro-Borges
Concrete structures damaged by corrosion along the Yucatan coast (Mexico) are usually repaired without following current specifications. Consequently, most repairs, especially those involving primers, are not always effective. There are still many concerns regarding the use of primers as a repair ... [Corrosion 67, 096001 (2011)] published Thu Sep 01, 2011.

[Read the rest of this article...]

Posted in: Corrosion
Actions: E-mail | Permalink |
22
E. Nunez Moran, G. S. Frankel, and Y. H. Kim
The localized corrosion resistance of three ferritic stainless steels containing 21% Cr and different amounts of Ca was determined and comparison was made with Type 304 (UNS S30400) stainless steel (SS) as a benchmark. The Ca content had an insignificant effect on the resistance to localized corro ... [Corrosion 67, 095005 (2011)] published Thu Sep 01, 2011.

[Read the rest of this article...]

Posted in: Corrosion
Actions: E-mail | Permalink |
22
F. El-Taib Heakal, O. S. Shehata, and N. S. Tantawy
Electrochemical measurements were used to characterize the effect of Nb and Cr on the corrosion behavior of two types of Al-bearing transformation-induced plasticity (TRIP) steels in naturally aerated sodium chloride (NaCl) solutions over a wide concentration range. In all cases, the open-circuit ... [Corrosion 67, 095006 (2011)] published Thu Sep 01, 2011.

[Read the rest of this article...]

Posted in: Corrosion
Actions: E-mail | Permalink |
08
X. Yong, C. Hou, and J. Wu et al.
The cavitation corrosion behavior and surface morphology of anodized aluminum alloy in 3.5% sodium chloride (NaCl) solution were investigated using weight loss and scanning electron microscopy. The electrochemical corrosion mechanism during cavitation corrosion was studied using electrochemical po ... [Corrosion 67, 095003 (2011)] published Thu Sep 01, 2011.

[Read the rest of this article...]

Posted in: Corrosion
Actions: E-mail | Permalink |
08
H. Kihira and M. Kimura
Since there is no infrastructure that is maintenance-free, both application technologies and public management systems for infrastructures, including financial plans for maintenance, are necessary to keep their public services safe and reduce the nation's social cost. One of the frontier models fo ... [Corrosion 67, 095002 (2011)] published Thu Sep 01, 2011.

[Read the rest of this article...]

Posted in: Corrosion
Actions: E-mail | Permalink |
08
F. Rouillard, F. Charton, and G. Moine
In the framework of a new generation of nuclear reactors, typically sodium fast reactors, supercritical carbon dioxide (CO2) with a Brayton cycle (at 550°C and 250 bars) is identified as a promising energy conversion system to replace the traditional steam generators. Nevertheless, the long-term i ... [Corrosion 67, 095001 (2011)] published Thu Sep 01, 2011.

[Read the rest of this article...]