Effect of Residual Stress of Dissimilar Metal Welding on Stress Corrosion Cracking of Bottom-Mounted Instrumentation Penetration Mock-Up

host posted on October 06, 2010 08:00

S. -W. Kim, H. -P. Kim, and J. -U. Jeong et al.
The present article is concerned with the effect of a residual stress induced by a dissimilar metal welding on stress corrosion cracking (SCC) of an Alloy 600 (UNS N06600) bottom-mounted instrumentation nozzle as a penetration mock-up in a pressurized water reactor. From a finite element analysis ( ... [Corrosion 66, 106001 (2010)] published Fri Oct 01, 2010.