H. -Y. Kim and H. J. Jang
The corrosion behavior of amorphous Co69Fe4.5Cr1.5Si10B15 alloy ribbon was investigated using potentiodynamic polarization tests in 0.001 M sulfuric acid (H2SO4) solution, 0.01 M ∼ 0.09 M sodium chloride (NaCl) solution, and solutions at pH levels from 3 to 13 made by mixing hydrochloric acid (HCl) ... [Corrosion 66, 116002 (2010)] published Mon Nov 01, 2010.

[Read the rest of this article...]

G. Ø. Lauvstad, R. Johnsen, and I. Asbjørnsen et al.
The resistance toward hydrogen-induced stress cracking (HISC) of forged and hot isostatically pressed (HIP) super duplex stainless steel (SDSS) according to UNS S32760 have been compared by slow strain rate testing (SSRT) under various environmental conditions, comprising exposure to a 3.5% sodium ... [Corrosion 66, 115004 (2010)] published Mon Nov 01, 2010.

[Read the rest of this article...]

D. D. N. Singh and A. Pandya
Corrosion inhibition of the self-assembled monolayer (SAM) of 1,2,3-Benzotriazole (BTAH) on virgin and sulfide-covered (tarnished) copper surfaces was studied using impedance, scanning electron microscopy, and Raman spectroscopy. SAM on preexisting sulfide film develops a more improved protection t ... [Corrosion 66, 115002 (2010)] published Mon Nov 01, 2010.

[Read the rest of this article...]

S. M. A. Hosseini, M. Salari, and M. Ghanei Motlagh et al.
The influence of organic compounds on the corrosion of stainless steel in 0.5 M sulfuric acid (H2SO4) was investigated using weight-loss and potentiodynamic polarization techniques, as well as open-cirucuit potential (OCP) measurements. The nature of the film formed and the adsorption mechanism, as ... [Corrosion 66, 115003 (2010)] published Mon Nov 01, 2010.

[Read the rest of this article...]

A. A. Ghoneim, M. A. Ameer, and A. M. Fekry et al.
The electrochemical corrosion and passivation behavior of four selected tin-silver alloys, xSn-Ag (x = 26, 50, 70, and 96.5 wt%) (II through V), in addition to their pure metallic components, Ag(I) and Sn(VI), were investigated in aqueous sodium hydroxide (NaOH) solution. The techniques used are li ... [Corrosion 66, 115001 (2010)] published Mon Nov 01, 2010.

[Read the rest of this article...]

S. Maddela, M. J. O'Keefe, and Y. -M. Wang et al.
The corrosion protection of cerium-based conversion coatings (CeCC) formed on AZ91D magnesium alloy has been studied using potentiodynamic polarization measurements, electrochemical impedance spectroscopy (EIS), and salt fog testing. The effect of acid (sulfuric acid [H2SO4]) and alkaline (sodium c ... [Corrosion 66, 115006 (2010)] published Mon Nov 01, 2010.

[Read the rest of this article...]

As a company dedicated to innovation and safety performance, Bayer MaterialScience LLC takes the steps necessary to help ensure the safe production, installation and function of its materials

[Read the rest of this article...]

PPG Industries has reached an agreement to acquire Bairun, a privately-held packaging coatings company in Gaoming District, Foshan, Guangdong in southern China. Financial terms were not disclosed. The deal is expected to close during the current quarter.

[Read the rest of this article...]

Krayden, Inc., a leading distributor of engineered materials, introduces Dow Corning's 3140 RTV Aerospace Coating

[Read the rest of this article...]

Surface Guard 96 series protective film features a polyolefin film coated with our proprietary and environmentally friendly SUR-Guard adhesive system. The 96 series protective film exhibits medium to low peel values that remain stable (and does not build) over time

[Read the rest of this article...]