Investigation of the Corrosion Protection of Ni Deposition and Subsequent Annealing Temperature with Flow of Nitrogen on AISI 304 and AISI 316 Stainless Steels

host posted on September 20, 2011 18:27

A. -R. Grayeli and H. Savaloni
AISI 304 (UNS S30400) and AISI 316 (UNS S31600) stainless steels were coated with a 250 run Ni film by electron beam deposition and post-annealed at different temperatures with a flow of 600 cm3 min−1 Ni. The samples were corrosion tested in 1.0 M sulfuric acid (H2SO4) solution using a potentiodyn ... [Corrosion 67, 105003 (2011)] published Sat Oct 01, 2011.