Dependence of Stress Corrosion Cracking of Alloy 690 on Temperature, Cold Work, and Carbide Precipitation—Role of Diffusion of Vacancies at Crack Tips

host posted on March 01, 2011 00:00

K. Arioka, T. Yamada, and T. Miyamoto et al.
The growth rate of stress corrosion cracking (SCC) was measured for cold-worked, thermally treated Alloy 690 (UNS N06690, CWTT690) and cold-worked, solution-treated Alloy 690 (CW ST 690) in hydrogenated pressurized water reactor (PWR) primary water under static load condition. Three important patt ... [Corrosion 67, 035006 (2011)] published Tue Mar 01, 2011.